求翻譯：The absorption spectra of Cr-containing Li2O- SiO2 transparent glass-ceramics was investigated. The crystalline phases precipitated in glass-ceramics are mainly Li2O?2SiO2 with a small amount of -SiO2 . The percent crystallinity and crystal sizes are 40–77 and 20–42 nm, respectively. A strong absorption band ascribed 是什么意思？ 待解決
 懸賞分：1
- 離問題結束還有
The absorption spectra of Cr-containing Li2O- SiO2 transparent glass-ceramics was investigated. The crystalline phases precipitated in glass-ceramics are mainly Li2O?2SiO2 with a small amount of -SiO2 . The percent crystallinity and crystal sizes are 40–77 and 20–42 nm, respectively. A strong absorption band ascribed
問題補充： |
|
2013-05-23 12:21:38
含鉻的吸收光譜li2o-SiO2透明玻璃陶瓷進行了調查。沉淀在玻璃陶瓷的晶相主要是li2o少量的二氧化硅2sio2。 ％的結晶度和晶粒尺寸為40-77和20-42納米，分別。強吸收帶歸因于Cr6 +的離子和弱D-D的吸收帶歸因于對Cr3 +離子在玻璃觀察電荷轉移。然而，出現新的吸收帶在600-700納米左右，這些頻段的吸收強度顯著增加（約15倍）后的結晶。有人建議，四面體CR4 +離子可能存在li2o-SiO2透明玻璃陶瓷。
|
|
2013-05-23 12:23:18
吸收頻譜的cr的li2o-sio2透明的玻璃-陶瓷進行了調查。 在玻璃的結晶性階段的陶瓷,主要是李2o?2sio2,可少量-sio2。 結晶度的百分比和水晶尺寸為40-77和20-42納米。 一個強大的吸收頻帶寬再接再厲,cr6+離子的電荷轉移和一個弱d-d吸收頻帶寬再接再厲,cr3+離子的玻璃。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
含 Cr Li2O-SiO2 透明玻璃陶瓷的吸收譜進行了調查。沉淀在微晶玻璃的晶相都有少量的 SiO2 的主要是 Li2O?2SiO2。百分比的結晶和晶粒大小分別是 40–77 和 20–42 nm。強烈吸收帶歸咎于六價鉻
|
|