求翻譯：選用的CHW-S60A焊絲與CHF102燒結焊劑，在F550Z海工板上進行焊接試驗及性能測試，其熔敷金屬屈服強度與抗拉強度分別達到610Mpa和685Mpa,這表明其強度完全達到與F550Z海工板匹配要求； 而其延伸率與低溫沖擊功達到27%和66J,這表明焊材熔敷金屬具有較好塑韌性和低溫沖擊韌性。這充分說明焊材匹配達到設計要求。是什么意思？ 待解決
 懸賞分：1
- 離問題結束還有
選用的CHW-S60A焊絲與CHF102燒結焊劑，在F550Z海工板上進行焊接試驗及性能測試，其熔敷金屬屈服強度與抗拉強度分別達到610Mpa和685Mpa,這表明其強度完全達到與F550Z海工板匹配要求； 而其延伸率與低溫沖擊功達到27%和66J,這表明焊材熔敷金屬具有較好塑韌性和低溫沖擊韌性。這充分說明焊材匹配達到設計要求。
問題補充： |
|
2013-05-23 12:21:38
Chw-optional the s60a wire and chf102 sintering flux, welding testing and performance testing the f550z marine board, the deposited metal yield strength and tensile strength, respectively 610mpa and 685mpa, which showed that its strength fully to work with f550z sea plate matching requirements; elon
|
|
2013-05-23 12:23:18
Choice of 60 A CHW - S CHF 102 solder and flux, the sintered F Z sea 550 welding on the board test and performance tests, its metal chymic yield strength to tensile strength, respectively 685 and 610 Mpa Mpa, which indicates the strength and reach 550 F Z harbor board match requirement, and the elon
|
|
2013-05-23 12:24:58
Selects the CHW-S60A welding wire and the CHF102 sintered flux, panel carries on the welding test and the performance test in the F550Z sea labor, its deposited metal yield strength and the tensile strength respectively achieved 610Mpa and 685Mpa, this indicated its intensity achieves completely wit
|
|
2013-05-23 12:26:38
Selection of CHW-S60A wire and CHF102 sintering flux, in F550Z sea workers Board Shang for welding test and the performance test, its melt with metal yield strength and tensile strength respectively reached 610Mpa and 685Mpa, this indicates that its strength full reached and F550Z sea workers Board
|
|
2013-05-23 12:28:18
正在翻譯，請等待...
|
湖北省互聯網違法和不良信息舉報平臺 | 網上有害信息舉報專區 | 電信詐騙舉報專區 | 涉歷史虛無主義有害信息舉報專區 | 涉企侵權舉報專區