求翻譯：As can be observed in Figure 5, the viscosity test results were almost inconclusive, as the results of temperature obtained for the mixing viscosity range were very similar to those of the original bitumen. This similarity is also confirmed by the penetration and softening point test results presented in Table 2.Theref是什么意思？ 待解決
 懸賞分：1
- 離問題結束還有
As can be observed in Figure 5, the viscosity test results were almost inconclusive, as the results of temperature obtained for the mixing viscosity range were very similar to those of the original bitumen. This similarity is also confirmed by the penetration and softening point test results presented in Table 2.Theref
問題補充： |
|
2013-05-23 12:21:38
正在翻譯，請等待...
|
|
2013-05-23 12:23:18
可以看出在圖5中,粘度測試結果幾乎沒有結果,因為結果的混合粘度的溫度范圍內獲得非常相似的原始瀝青。 這種相似之處是也證實了滲透和軟化點測試結果列于表2.因此,在溫度降低的定義在本質上根據compactability測試結果。
|
|
2013-05-23 12:24:58
正在翻譯，請等待...
|
|
2013-05-23 12:26:38
圖 5 中可以看出，粘度測試結果是幾乎未有定論，溫度為混合粘度范圍獲得的結果非常類似的原始瀝青。這種相似性，也證實了滲透和軟化點測試結果提交 2.Therefore 表中，溫度下降實質根據定義緊實率測試結果。生產的 140oC 和 130oC 的 WMA 混合物進行這些測試 （分別是 25oC 和 35oC 低于常規的混合物的溫度） 為了比較空隙量和 WMAs 和瀝青混合料水敏感性
|
|
2013-05-23 12:28:18
和在表5能被觀察，黏度測試結果是幾乎非決定性的，因為為混合的黏度范圍得到的溫度的結果于那些是非常相似的原始的瀝清。 這相似性由滲透也證實，并且軟化點在表提出的測試結果2.Therefore里，降溫根據compactability測試結果實質上被定義了。 這些測試在WMA混合物被執行了被生產在140oC和130oC (分別， 25oC和35oC在常規混合物的溫度之下)為了比較空隙內容和WMAs和HMA的水敏感性
|
湖北省互聯網違法和不良信息舉報平臺 | 網上有害信息舉報專區 | 電信詐騙舉報專區 | 涉歷史虛無主義有害信息舉報專區 | 涉企侵權舉報專區