求翻譯：The surface modification procedure was as follows. Appropriate amount of commercial CaO particles were added into trimethylchlorosilane(TMCS) solution in hexane under stirring at room temperature for activation. After 24 h, the mixture was separated and washed with hexane in order to remove the excess silane,and then t是什么意思？ 待解決
 懸賞分：1
- 離問題結束還有
The surface modification procedure was as follows. Appropriate amount of commercial CaO particles were added into trimethylchlorosilane(TMCS) solution in hexane under stirring at room temperature for activation. After 24 h, the mixture was separated and washed with hexane in order to remove the excess silane,and then t
問題補充： |
|
2013-05-23 12:21:38
表面改性過程如下。適量商業曹顆粒的加入三甲基氯硅烷（TMCS）在正己烷溶液，攪拌下于室溫激活。 24小時后，被分離的混合物，用正己烷沖洗，以消除多余的硅烷，然后改性CaO后，真空干燥過程中得到的。
|
|
2013-05-23 12:23:18
表面上是修改程序,如下所示。 適當的金額增加了顆粒的商業曹成trimethylchlorosilane(tmcs)的解決方案,在室溫下己烷在攪動激活。 24小時后,得到的混合物分離和清洗,以去除多余己烷在silane”,然后修改后得到了曹是一個干燥真空處理流程。
|
|
2013-05-23 12:24:58
表面修改做法如下是。 適當的相當數量商業CaO微粒在己烷增加了入三甲基氯硅烷(TMCS)解答在攪動在室溫之下為活化作用。 在24 h以后，混合物分離并且洗滌與己烷為了去除剩余硅酮，修改過的CaO在一個干燥真空過程以后然后得到了。
|
|
2013-05-23 12:26:38
表面改性的程序是，如下所示。正己烷在室溫為激活攪拌下的 trimethylchlorosilane(TMCS) 解決方案，加入了適當的商業 CaO 顆粒量。24 小時后, 將混合物分隔，并為了刪除多余的硅烷，正己烷用水洗并且然后改性的曹得到真空干燥后。
|
|
2013-05-23 12:28:18
表面的更改程序是如下。商業 CaO 微粒的適當的數量在為激活以房間溫度走動下被加到在己烷中的 trimethylchlorosilane(TMCS) 解決方案中。在 24 h 之后，混合有己烷被分開和洗以撤銷過多的 silane，然后被修改的 CaO 在一個干燥真空過程之后獲取。
|
湖北省互聯網違法和不良信息舉報平臺 | 網上有害信息舉報專區 | 電信詐騙舉報專區 | 涉歷史虛無主義有害信息舉報專區 | 涉企侵權舉報專區