求翻譯：當加Y量為0.9%時, 合金的延伸率達到最大, 為14.6%。經過T6熱處理后, 合金的抗拉強度較鑄態均得到了明顯提高, 而延伸率有所下降。是什么意思？ 待解決
 懸賞分：1
- 離問題結束還有
當加Y量為0.9%時, 合金的延伸率達到最大, 為14.6%。經過T6熱處理后, 合金的抗拉強度較鑄態均得到了明顯提高, 而延伸率有所下降。
問題補充： |
|
2013-05-23 12:21:38
Plus y 0.9%, the elongation of the alloy reaches the maximum, at 14.6%. After t6 heat treatment, the tensile strength than the cast has been significantly improved, while the elongation declined.
|
|
2013-05-23 12:23:18
When you load the Y amount is 0.9 % of the alloy, when extended to the maximum rate to 14.6 % . After T 6 heat-treated, alloy casting patterns for tensile strength is the apparent increase in elongation rate of decline.
|
|
2013-05-23 12:24:58
When adds the Y quantity is 0.9%, the alloy elongation ratio achieved biggest, is 14.6%.After the T6 heat treatment, the alloy tensile strength compared the cast condition to obtain the distinct enhancement, but the elongation ratio had the drop.
|
|
2013-05-23 12:26:38
When you add y to 0.9%, alloy elongation reaches the maximum, to 14.6%. After T6 heat treatment, the tensile strength than cast alloy have been markedly improved, extension rate declined.
|
|
2013-05-23 12:28:18
正在翻譯，請等待...
|
湖北省互聯網違法和不良信息舉報平臺 | 網上有害信息舉報專區 | 電信詐騙舉報專區 | 涉歷史虛無主義有害信息舉報專區 | 涉企侵權舉報專區